[KMg3(AlSi3O10)F2] -Synthetized Fluorphlogopite Mica, 8x 8x0.2 thick (mm), as cleaved Orientation 0001 1mm (Thickness)

1mm (Thickness)

(+/- 10%) with roughness: ~5 nm RMS

YLJ-5TA) can be used to apply accurate force on split cell

Orientation: Y-cut with 36 degree off

[KMg3(AlSi3O10)F2] -Synthetized Fluorphlogopite Mica, 8x 8x0.2 thick (mm), as cleaved Orientation 0001 1mm (Thickness)Synthetic fluorophlogopite is obtained by cooling and devitrification of chemical raw materials by high temperature melting. The single wafer fraction is KMg3(AlSi3O10)F2, which belongs to the monoclinic system and is a typical layered silicate. KMg3(AlSi3O10)F2 is a typical layered silicate. Many of its properties are superior to natural mica. For example, when the temperature is higher than 1200C, the volume resistivity of synthetic fluorophlogopite